Calculation base for hardness and tensile strength
Calculation of the Vickers hardness out of the Rockwell hardness (after Quarnström):
Hardness(HV) = 223*Hardness(HRC)+14500 / 100-Hardness(HRC)
Conversion of the tensile strength out of the Vickers hardness after DIN 501500:
Rm(MPa) = 3,206358 * Hardness(HV) - Area of Validity 80 - 430HV
| Brinell hardness |
Tensile strength N/mm2 |
Vickers hardness HV (F+98N) |
Rockwell hardness HRC |
| 76,0 | 255 | 80 | - |
| 80,7 | 270 | 85 | - |
| 85,5 | 285 | 90 | - |
| 90,2 | 305 | 95 | - |
| 95,0 | 320 | 100 | - |
| 99,8 | 335 | 105 | - |
| 105 | 350 | 110 | - |
| 109 | 370 | 115 | - |
| 114 | 385 | 120 | - |
| 119 | 400 | 125 | - |
| 124 | 415 | 130 | - |
| 128 | 430 | 135 | - |
| 133 | 450 | 140 | - |
| 138 | 465 | 145 | - |
| 143 | 480 | 150 | - |
| 147 | 495 | 155 | - |
| 152 | 510 | 160 | - |
| 156 | 530 | 165 | - |
| 162 | 545 | 170 | - |
| 166 | 560 | 175 | - |
| 171 | 575 | 180 | - |
| 176 | 595 | 185 | - |
| 181 | 610 | 190 | - |
| 185 | 625 | 195 | - |
| 190 | 640 | 200 | - |
| 195 | 660 | 205 | - |
| 199 | 675 | 210 | - |
| 204 | 690 | 215 | - |
| 209 | 705 | 220 | - |
| 214 | 720 | 225 | - |
| 219 | 740 | 230 | - |
| 223 | 755 | 235 | - |
| 228 | 770 | 240 | 20,3 |
| 233 | 785 | 245 | 21,3 |
| 238 | 800 | 250 | 22,2 |
| 242 | 820 | 255 | 23,1 |
| 247 | 835 | 260 | 24,0 |
| 252 | 850 | 265 | 24,8 |
| 257 | 865 | 270 | 25,6 |
| 261 | 880 | 275 | 26,4 |
| 266 | 900 | 280 | 27,1 |
| 271 | 915 | 285 | 27,8 |
| 276 | 930 | 290 | 28,5 |
| 280 | 950 | 295 | 29,2 |
| 285 | 965 | 300 | 29,8 |
| 295 | 995 | 310 | 31,0 |
| 304 | 1030 | 320 | 32,2 |
| 314 | 1060 | 330 | 33,3 |
| 323 | 1095 | 340 | 34,4 |
| Brinell hardness |
Tensile strength N/mm2 |
Vickers hardness HV (F+98N) |
Rockwell hardness HRC |
| 333 | 1125 | 350 | 35,5 |
| 342 | 1155 | 360 | 36,6 |
| 352 | 1190 | 370 | 37,7 |
| 361 | 1220 | 380 | 38,8 |
| 371 | 1255 | 390 | 39,8 |
| 380 | 1290 | 400 | 40,8 |
| 390 | 1320 | 410 | 41,8 |
| 399 | 1350 | 420 | 42,7 |
| 409 | 1385 | 430 | 43,6 |
| 418 | 1420 | 440 | 44,5 |
| 428 | 1455 | 450 | 45,3 |
| 437 | 1485 | 460 | 46,1 |
| 447 | 1520 | 470 | 46,9 |
| (456) | 1555 | 480 | 47,7 |
| (466) | 1595 | 490 | 48,4 |
| (475) | 1630 | 500 | 49,1 |
| (485) | 1665 | 510 | 49,8 |
| (494) | 1700 | 520 | 50,5 |
| (504) | 1740 | 530 | 51,1 |
| (513) | 1775 | 540 | 51,7 |
| (523) | 1810 | 550 | 52,3 |
| (532) | 1845 | 560 | 53,0 |
| (542) | 1880 | 570 | 53,6 |
| (551) | 1920 | 580 | 54,1 |
| (561) | 1955 | 590 | 54,7 |
| (570) | 1995 | 600 | 55,2 |
| (580) | 2030 | 610 | 55,7 |
| (589) | 2070 | 620 | 56,3 |
| (599) | 2105 | 630 | 56,8 |
| (608) | 2145 | 640 | 57,3 |
| (618) | 2180 | 650 | 57,8 |
| - | - | 660 | 58,3 |
| - | - | 670 | 58,8 |
| - | - | 680 | 59,2 |
| - | - | 690 | 59,7 |
| - | - | 700 | 60,1 |
| - | - | 720 | 61,0 |
| - | - | 740 | 61,8 |
| - | - | 760 | 62,5 |
| - | - | 780 | 63,3 |
| - | - | 800 | 64,0 |
| - | - | 820 | 64,7 |
| - | - | 840 | 65,3 |
| - | - | 860 | 65,9 |
| - | - | 880 | 66,4 |
| - | - | 900 | 67,0 |
| - | - | 920 | 67,5 |
| - | - | 940 | 68,0 |
(Werte in Klammern mit Hartmetallkugel). Die Angaben beziehen sich auf normale Stähle mit Ausnahme der Austenite und kaltumgeformtem Material. Die Vickershärte wird mit einer Diamantpyramide von 136° Spitzenwinkel gemessen. Bei der Brinell-Prüfung wird die Belastungsquote P/D2=30 vorausgesetzt (P= Belastung in kg; D= Kugeldurchmesser in mm).